PA6 GF30
XINYITE
PA6 GF30 plastic granules, also known as Polyamide 6 with 30% glass fiber reinforcement, are widely used in the manufacturing of electrical parts. The addition of glass fibers enhances the mechanical properties of the plastic, making it stronger and stiffer compared to unfilled PA6.
The electrical industry often chooses PA6 GF30 for its excellent electrical insulating properties and high heat resistance. It also offers good chemical resistance, dimensional stability, and low moisture absorption. These characteristics make it suitable for various electrical components, such as connectors, housings, switches, and sockets.
When using PA6 GF30 plastic granules for electrical parts, it is important to ensure proper processing techniques to maintain the desired mechanical and electrical properties. Injection molding is a common method used to produce complex shapes with high precision.
PA6 GF30 plastic granules, also known as Polyamide 6 with 30% glass fiber reinforcement, are widely used in the manufacturing of electrical parts. The addition of glass fibers enhances the mechanical properties of the plastic, making it stronger and stiffer compared to unfilled PA6.
The electrical industry often chooses PA6 GF30 for its excellent electrical insulating properties and high heat resistance. It also offers good chemical resistance, dimensional stability, and low moisture absorption. These characteristics make it suitable for various electrical components, such as connectors, housings, switches, and sockets.
When using PA6 GF30 plastic granules for electrical parts, it is important to ensure proper processing techniques to maintain the desired mechanical and electrical properties. Injection molding is a common method used to produce complex shapes with high precision.
PROPERTIES | Units | METHOD | PA6 GF30 |
Tensile Strength | Mpa | ISO527 | 130 |
Mold Shrinkage | % | ISO2577 | 0.4-1.1 |
Flexural Strength | Mpa | ISO178 | 180 |
Flextural Modulus | Mpa | ISO178 | 6500 |
Notched IZOD Impact at 23℃ | KJ/㎡ | ISO180 | 11 |
Density | g/cm3 | ISO1183 | 1.29(±0.01) |
Flammability | - | UL94 | HB |
Melt Flow Index | g/10min | ISO1133 | / |
Heat deflection temperature (0.45MPA) | ℃ | ISO75 | 210 |
PROPERTIES | Units | METHOD | PA6 GF30 |
Tensile Strength | Mpa | ISO527 | 130 |
Mold Shrinkage | % | ISO2577 | 0.4-1.1 |
Flexural Strength | Mpa | ISO178 | 180 |
Flextural Modulus | Mpa | ISO178 | 6500 |
Notched IZOD Impact at 23℃ | KJ/㎡ | ISO180 | 11 |
Density | g/cm3 | ISO1183 | 1.29(±0.01) |
Flammability | - | UL94 | HB |
Melt Flow Index | g/10min | ISO1133 | / |
Heat deflection temperature (0.45MPA) | ℃ | ISO75 | 210 |