PP V0
XINYITE
Flame retardant PP material is a modified PP, which is mainly composed of environmentally friendly bromine-tantalum flame retardant system and halogen-free environment-friendly phosphorus and nitrogen systems.
This material has exceptional flame resistance properties. It is designed to self-extinguish when exposed to fire, making it an ideal choice for applications where fire safety is crucial. Our XINYITE material undergoes rigorous testing to meet stringent fire safety standards, providing manufacturers with peace of mind and ensuring the safety of end-users.
PP V0 material has emerged as a top choice for manufacturers looking for a combination of flame resistance, high temperature resistance, mechanical strength, chemical resistance, and cost-effectiveness. Its ability to meet stringent safety standards, withstand extreme conditions, and offer excellent durability has made it a preferred material across various industries.
Flame retardant PP material is a modified PP, which is mainly composed of environmentally friendly bromine-tantalum flame retardant system and halogen-free environment-friendly phosphorus and nitrogen systems.
This material has exceptional flame resistance properties. It is designed to self-extinguish when exposed to fire, making it an ideal choice for applications where fire safety is crucial. Our XINYITE material undergoes rigorous testing to meet stringent fire safety standards, providing manufacturers with peace of mind and ensuring the safety of end-users.
PP V0 material has emerged as a top choice for manufacturers looking for a combination of flame resistance, high temperature resistance, mechanical strength, chemical resistance, and cost-effectiveness. Its ability to meet stringent safety standards, withstand extreme conditions, and offer excellent durability has made it a preferred material across various industries.
PROPERTIES | Units | METHOD | PP V0 |
Tensile Strength | Mpa | ISO527 | 28 |
Mold shrinkage | % | ISO2257 | 1 |
Flexural Strength | Mpa | ISO178 | 35 |
Flextural Modulus | Mpa | ISO178 | 2200 |
Notched IZOD Impact at 23℃ | KJ/㎡ | ISO180 | 5 |
Density | g/cm3 | ISO1183 | 1.36 |
Flammability | - | UL94 | V0 |
Melt Flow Index | g/10min | ISO1133 | 10 |
Heat deflection temperature (0.45MPA) | ℃ | ISO75 | 110 |
PROPERTIES | Units | METHOD | PP V0 |
Tensile Strength | Mpa | ISO527 | 28 |
Mold shrinkage | % | ISO2257 | 1 |
Flexural Strength | Mpa | ISO178 | 35 |
Flextural Modulus | Mpa | ISO178 | 2200 |
Notched IZOD Impact at 23℃ | KJ/㎡ | ISO180 | 5 |
Density | g/cm3 | ISO1183 | 1.36 |
Flammability | - | UL94 | V0 |
Melt Flow Index | g/10min | ISO1133 | 10 |
Heat deflection temperature (0.45MPA) | ℃ | ISO75 | 110 |
![]() | ![]() | ![]() | ![]() |
Electrical box | Electrical switches | Motor cover | Wire clamp |
![]() | ![]() | ![]() | ![]() |
Electrical box | Electrical switches | Motor cover | Wire clamp |